Geomembranes Slavros HDPE

Description

Description The rolled polymer insulating material of the “Slavros” geomembrane is intended for carrying out waterproofing works of various degrees of complexity, protection against corrosion and waterproofing of concrete structures, creation of antifiltration screens.

HDPE geomembrane is characterized by increased durability and resistance to aggressive chemicals, which allows the use of HDPE geomembrane on a large, flat surface: landfills for household and industrial waste (solid and liquid), protection of surfaces from any material, construction of drinking water tanks and so on.

For the manufacture of geomembranes use lowpressure polyethylene or high-pressure polyethylene.

Main applications of geomembrane:

•       waterproofing of layers of the road pavement, lower layers of the roads and railways;

•       storage of industrial and domestic waste (landfills);

•       storage tanks of industrial and agricultural enterprises;

•       anti-filtration protection of storage tanks for petroleum products, automotive gas stations;

•       drinking water reservoirs, irrigation ponds and canals, rainwater collection reservoirs, fire reservoirs;

•       impervious screens;

•       corrosion protection, waterproofing and gas insulation of concrete structures;

•       industrial sludge collectors;

•       storage areas for hazardous substances;

•       soil pollution insulators;

•       dams;

•       lagoons of manure reservoirs;

•       storage of dry products;

•       architectural and landscape ponds;

•       waterproofing inversion roofs;

•       tunnels.

The main advantages of using the Slavros geomembrane:

  • ease of transportation and storage of materials;
  • absolute water tightness;
  • possibility of the vertical anti-filtration barrier;
  • high resistance to mechanical stress;
  • chemical resistance to a wide range of pollutants;
  • service life more than 80 years;
  • material is absolutely nontoxic, is not dangerous to human health, animals, fish and does not change its properties during the entire service life.

Name

indicator

HDPE membranes

LLDPE membranes

1. Density, g / cm3

≥0,940

≤0,939

2. Strength at

stretching at +20°С,

kN / m, not less,

with sheet thickness, mm: - 1,00

                                         - 1,50

                                         - 2,00

                                         - 2,50

                                         - 3,00

27

40

53

67

80

27

40

53

66

80

3.Elongation at break at plus 20°С,

not less, %

700

800

4. Tensile yield strength at temperature + 20 ° С, not less, MPa

17,0

15,0

5. Yield strength,

kN / m, not less,

with sheet thickness, mm: - 1,00

                                         - 1,50

                                         - 2,00

                                         - 2,50

                                         - 3,00

15

22

29

37

44

-

6.Elongation at yield,

not less, %

12

-

7. Secant modulus at 2% deformation, N / mm, not more,

with sheet thickness, mm: - 1,00

                                         - 1,50

                                         - 2,00

                                         - 2,50

                                         - 3,00

-

420

630

840

1050

1260

8. Tear resistance,

N, not less,

with sheet thickness, mm: - 1,00

                                         - 1,50

                                         - 2,00

                                         - 2,50

                                         - 3,00

125

187

249

311

374

100

150

200

250

300

9. Resistance to static punching, N, not less, at sheet thickness, мм:                                 

                                         - 1,00

                                         - 1,50

                                         - 2,00

                                         - 2,50

                                         - 3,00

150

220

330

440

540

150

280

400

500

580

10. Puncture strength,

H, not less, at sheet thickness, мм:                         

                                         - 1,00

                                         - 1,50

                                         - 2,00

                                         - 2,50

                                         - 3,00

320

480

640

800

960

250

370

500

620

750

11. Tear resistance, N, not less, with thickness

sheet mm:                       - 1,00

                                         - 1,50

                                         - 2,00

                                         - 2,50

                                         - 3,00

140

210

265

350

420

120

200

250

320

400

  12. Flexibility on a rod with a radius of 5 mm, at a temperature of minus 60 ºС

On the sample surface
there should be no cracks
and other visible defects

On the sample surface
there should be no cracks
 and other visible defects

  13. Loss of strength after 30 freeze-thaw cycles,% of the initial value, not more than

10

10

  14. Loss of strength after 90 days of aging at 85 ºС,% of the initial value, not more than

45

50

  15. Loss of strength after 400 hours of exposure to UV,% of the initial value, not more than

15

20

16. Combustibility:

- highly flammable

- highly flammable

Duration of self-burning for more than 300 seconds

Duration of self-burning no more than 30 seconds

Duration of self-burning for more than 300 seconds

Duration of self-burning no more than 30 seconds